湘钢方板坯连铸机技术特点和生产实践 杨建华 尹志强 何航 (湖南华菱湘潭钢铁集团公司 湘潭 411101 中国) 摘要：本文介绍了湘钢方板坯连铸机的主要技术参数和技术特点, 方板坯连铸机的生产实践表明：方板坯各项生产技术经济指标不断攀升，产能已经超过了设计能力，板坯和方坯的平均连浇炉数分别稳定在16～18炉和10炉，板坯采用全自动开浇，而方坯的自动开浇成功率基本达到100%。方坯和板坯的表面质量和内部质量良好，铸坯平均合格率达到99.5%以上。板坯和方坯的最高低倍合格率分别达到96.1%和100%。 关键词：方板坯连铸机 技术特点 生产实践 The Technical Characteristics and Production Practice with the New Slab/Triple Bloom Caster at Xianggang YANG Jian-hua YIN Zhi-qiang HE Hang (Hunan Valin Xiangtan Iron and Steel Co., Ltd., Xiangtan 411101, China) ABSTRACT：In this paper, the main technical characteristics and parameters of the combi-caster are presented. The production practice of the comb-caster shows: main techno-economic index of combi-caster was increased. The outputs have exceeded the design productive capacity. The average casting sequence for slab and bloom was 16～18 heats and 10 heats. The automatic cast starting always is adopted when casting slab and the automatic cast starting rates keep 100% basically for blooms, the surface quality and internal quality for slab and bloom was excellent, Average qualification rate of slab and bloom was more than 99.5%. The sulfur-print samples maximum qualification rate got to 96.1% for slab and 100 % for bloom. Key Words: Combi-caster Technical Characteristics Production Practice 1 前言 2007年5月，中国第一套（世界第三条套）该VAI的方板坯连铸机在湘潭钢铁有限责任公司（以下简称湘钢）正式建成投产。该铸机采用世界先进工艺技术。同一台铸机通过更换结晶器和弯曲段，既生产方坯，又可以生产板坯。该铸机采用直结晶器、带液芯的多点连续矫直技术、动态轻压下技术、SMART扇形段以及电磁搅拌技术等先进技术。至投产以来，该铸机运行良好，各项经济技术指标不断攀升，取得了良好的经济效益。 2 方板坯连铸机主要技术参数 2.1 方板坯连铸机主要参数 方板坯连铸机的主要技术参数如表1。 2.2 方板坯连铸机的主要特点 2.2.1 特殊的中包设计 方坯和板坯都采用梯型中间包，方坯中包上设计有3个彼此独立的开孔，用于安装浸入式水口。 浇注板坯时，采用浸入式水口快换装置，而浇注方坯则采用事故闸板。如图1。 图1 方板坯铸机梯型中间包 Figure 1 Tapeze-type tundish for cobi-caster 表1 方板坯连铸机主要技术参数 Table 1 Main data of the combi-caster 项目 性能或参数 连铸机机型 弧形，带液芯多点连续矫直 机数 1机 流数 板坯 1流 方坯 3流 弧半径 10m 冶金长度 36.5m 流间距（方坯） 985mm 中间包类型 型中间包 中间包容量 45t 结晶器类型 直结晶器 结晶器铜板长度 900mm 结晶器液面控制 方坯 放射性同位素Co60 板坯 电磁涡流式 浇铸断面 板坯 厚度：260mm，300mm； 宽度：1200～2300mm 方坯 300×4