2007 年全国塑性加工理论与新技术学术研讨会 2007 年 5 月 沈阳 累积复合轧制中 1060 铝组织和性能的演变 张 兵，王快社，袁守谦，吕 爽，张西锋 (西安建筑科技大学材料工程学院,陕西 西安,710055) 摘 要：采用累积轧制方法在室温下对1060工业纯铝进行变形，分析了变形前后其微观组织和力学性能。实验结果 表明，随着累积叠轧道次的增加，材料的抗拉强度和硬度提高，延伸率先降后升；材料在等效真应变为 5.6 的剧烈 变形条件下得到了平均晶粒尺寸为520nm 的超细晶组织。 关键词: 剧烈塑性变形；累积叠轧；工业纯铝；微观组织；力学性能 Evolvement of Microstructure Property for 1060 －Al during Accumulative Roll Bonding(ARB) Process ZHANG Bing, WANG Kuaishe, YUAN Shouqian, LV Shuang, ZHANG Xifeng (Dept. of Material Engineer, Xi’an University of Architecture Technology, Xi’an710055, China) Abstract: In this paper, 1060 Al was deformed by accumulated rolling bonding (ARB). The microstructure and mechanical property of the 1060 Al both of Annealed and after ARB were studied. The results shown that as the ARB passes increasing, both the material’s micro hardness and tensile strength were increasing; the elongation dropped at first, and increased after reached the lowest. The grain were fine and average grains size was 520 nm when the accumulated strain was 5.6. Key words: severe plastic deformation (SPD); accumulative roll bonding (ARB); commercially pure aluminum; microstructure; mechanical property 1 前言 近年来，采用剧烈塑性变形（SPD, Severe Plastic Deformation ）的方法来获得晶粒尺寸小于 1 μm 块体超细晶材料引起人们的广泛关注。超细晶结构的金属材料相对于传统金属材料在室温下具 有高强度和高韧性，在低温或高变形速率下具有超塑性和一定的物理特性[1-3]，从而改善材料的综合 性能。现已知的 SPD 方法有：高压扭转法(HTP, High Pressure Torsion)[4]、等通道角挤(ECAP, Equal [5] [6] channel angular pressing) 、累积轧制（ARB, accumulative roll-bonding ） 、多向锻造法（MF, Multiple [7] [8] Forging ） 、往复挤压（CEC,Cyclic Extrusion Compression or Reciprocal Extrusion ） 等，这些方法 都是通过对块体金属材料直接进行剧烈的塑性变形，材料内部的晶粒发生反复的相互剪切变形，在 内摩