镁锂合金真空电阻炉熔炼工艺.pdfVIP

学兔兔 镁锂合金真空电阻炉熔炼工艺 董天顺，刘金海，陈 刚，郑振太 (河北工业大学材料学院，天津 300132) 摘要：镁锂合金很容易被氧化，故镁锂合金的熔炼比较困难。采用真空电阻炉，分别以三种工 艺熔炼了不同成分的镁锂合金，并对得到的合金成分进行了检测分析，最终确定了分别适合于 Li含量较高和较低情况下的熔炼工艺。 关键词：镁锂合金；真空电阻炉；熔炼工艺 中图分类号：TF822 文献标识码：A 文章编号：1673—3320(2013)03-0005-03 Melting Process of Mg·Li Alloy Using Vacuum Electric Resistance Furnace Dong Tianshun，Liu Jinhai，Chen Gang，Zheng Zhentai (School of Material Science and Engineering，Hebei University of Technology,Tianjin 3001 32，China) Abstract：Mg—Li alloy is difficult to be melted as it is easily oxidized．The Mg—Li alloys with different chemical compositions were melted using three processes in vacuum electric resistance furnace． Subsequently,the chemical compositions of Mg—Li alloy were studied．Eventually,melting processes respectively suitable for higher and lower Li content were determined． Key words：Mg—Li alloy；vacuum electric resistance fumace；melting process 镁锂合金凭借其众多优异的特性而受到日益 广泛的关注[1-2】，但是镁锂合金中高活性的金属镁 和金属锂都很容易被氧化，并且产生的氧化膜致 密度小于1，不能阻止氧化的继续进行，故镁锂 合金的熔炼比较困难。总体来说，其熔炼中的保 护方法主要有两种，一种是通过使用覆盖剂把液 态金属与空气隔离，另一种是使用惰性气体氩作 为保护气体。其中使用惰性气体保护的方法比较 好，它可以避免因使用覆盖剂而产生的缺陷[3_ 】。 本试验采用真空电阻炉抽真空后充氩气保护的方 法熔炼镁锂合金，并对不同原料添加方法的合金 冶金质量进行了研究。 图1 真空电阻炉的总体结构图 炉体部分是整个真空电阻熔炼炉的核心。炉 1 试验设备及方法 盖和炉身组成了熔炼炉的真空室，在炉盖上安置 1．1 真空电阻炉结构 了合金加料装置和搅拌装置，并有两个观察窗， 本试验所采用的真空电阻炉主要由五部分组 在熔炼过程中可通过观察窗观察炉内情况。加热 成：炉体部分、真空系统、控制系统、冷却水系 元件为钼片，钼片和坩埚之间通过一层镁砂绝 统和电源部分。其整体结构如图1所示。 缘，并一起固定在坩埚支架上组成加热体。坩埚 收稿日期：2012—1卜20 作者简介：董天顺 (1968一)，男，博士，硕士生导师，主要从事铝、镁合金及其复合材料的研究 2ol3年第3期 I 5