铝矾土粉料结构特性对铸型涂料性能的影响.pdfVIP

学兔兔 铝矾土粉料结构特性对铸型涂料性能的影响 朱 筠 (上海市机械制造工艺研究所有限公司，上海 200072) 摘要：通过涂料配比试验，分析了铝矾土粉料的体积密度、表面酸碱性及多孔结构对铸型涂料 性能的影响。结果表明，采用高体积密度的铝矾土粉料可得到涂层致密的砂型醇基涂料；根据 铝矾土粉料表面酸碱性合理选择聚合磷酸盐的种类，可使砂型水基涂料具有良好的稳定性；铝 矾土粉料的多孔结构有利于改善消失模涂料的透气性。 关键词：铸型涂料；铝矾土；体积密度；表面酸碱性；多孔结构 中图分类号：T6221 文献标识码：A 文章编号：1673-3320(2010)01—0005—03 Effects of Structural Characteristics f．cr Bauxite on Performances of Mold Coatings Zhu Yun (Shanghai Machine Building Technology Institute Co．，Ltd．，Shanghai 200072，China) Abstract：The effects of bulk density,surface acidity／basicity and porous structure for bauxite on the performances of mold coatings were analyzed by the test for coatings．The results show that the alcohol— base sand coating with denser coat iS obtained by the bauxite with higher bulk densitN selecting the appropriate poly—phosphate by the surface acidity／basicity of bauxite makes the water-base sand coming with be~er stability,and the porous structure for bauxite iS helpful to improve the permeability of EPC coatings． Key words：mold coating；bauxite；bulk density；surface acidity／basicity；porous structure 铝矾土粉料属Al—Si系耐火材料，主要矿物组 1 铝矾土粉料的体积密度 成为莫来石 (3AI O3·2SiO )。目前用于铸型涂料 体积密度是耐火材料的质量与其总体积的比 的铝矾土粉料是铝矾土原矿经1 300～1 500℃高 值。它表征了耐火材料的致密程度【z】。体积密度 温煅烧得到的熟料，再经破碎、筛选而成，其耐 高的耐火材料，其致密度高，高温性能好。YB／T 火度随Al 0，含量的增加和煅烧温度的升高而提 5179—2005规定了用于耐火材料的高铝矾土熟料 高…。在浇注条件下铝矾土不易和金属氧化物生 的理化指标，不同化学成分的高铝矾土熟料均有 成低熔点化合物，同时金属液及其氧化物对铝矾