酯硬化碱性酚醛树脂砂模拟再生试验.pdfVIP

学兔兔 酯硬化碱性酚醛树脂砂模拟再生试验 张 江 (南通强鸿铸造有限公司，江苏 南通 226351) 摘要：通过对酯硬化碱性酚醛树脂旧砂的模拟再生试验，分析了再生前后砂样的灼烧减量、发 气量等性能的变化，以及对型砂强度的影响因素。结果表明：采用模拟再生工艺可使再生砂 回收率达到95％左右；在再生砂中加入质量分数1 0％～2O％的新砂，可明显提高再生砂的黏结强 度，为更好运用酯硬化碱性酚醛树脂砂生产高强度钢种的铸件提供旧砂再生工艺方案。 关键词：碱性酚醛树脂砂；有机酯；再生砂 中图分类号：TG221 ．2 文献标识码：A 文章编号：1673—3320(2010)05-0004-02 Pilot TriaI Reclamation of Ester Cured Alkaline Phenolic Resin Sand Zhang Jiang (Nantong Qianghong Casting Co．，Ltd．，Nantong 226351，Jiangsu，China) Abstract：The used ester cured alkaline phenolic resin sand was tested．The ignition loss and gas evolution as well as influence of sand strength before and after reclamatiOn have been compared．The test result shows that strength of reclaimed sand can be improved at 95％recovered sand and 1 0％．20％ new sand．This result provide basis for the large SCale reclamation process of ester cured phenolic resin sand for high strength steel casting． Key words：alkaline phenolic resin sand；ester；sand reclamation 对于高强度钢种的铸件 (如新产品开发中的 2．24％，福士科H20有机酯为树脂质量的23．03％。 履带板、上钳体、驱顶箱体等)，一般采用酯硬化 2)试验方案：根据国外资料介绍，酯硬化碱 碱性酚醛树脂硅砂造型工艺，然而，酯硬化碱性 性酚醛树脂砂膜属于塑性膜，再生处理时需要将 酚醛树脂砂的生产成本较高。本文通过选取浇注 旧砂预热至320,~350℃，再进行机械摩擦 (运用 上钳体后的酯硬化碱性酚醛树脂砂的旧砂，测试 $2004型碗形混砂机)，经除尘后效果明显。 系统模拟再生后的型砂性能，由此探讨其再生工 旧砂的模拟再生工艺如图1所示。 艺。 样砂l-,q破碎 l过筛l_三型 塑型 I力口热 1 试验材料 1)旧砂 ：根据浇注后酯硬化碱性酚醛树脂旧 砂的受热程度，分别选取三种样砂：高温区域的 砂型记为III层砂，中温区为II层砂，低温区 (未 图1模拟再生工艺流程 受高温)为I层砂，I、II、III层砂各取5 kg： 2 试验设备 模拟再生后的砂样分别记为I’、II’、III’。旧砂的 原型砂配方 ：常州益强硅砂 (