含铬铜合金管坯水平连铸工艺探讨.pdfVIP

学兔兔 铸造工艺 含铬铜合金管坯水平连铸工艺探讨 孙国臣 (一汽铸造有限公司技术中心，吉林 长春 130062) 摘要：介绍了采用离心铸造、水平连铸、压力挤制等方法获得铜合金管坯的工艺特点。对水平 连铸方法拉拔含铬铜合金管坯存在的技术问题进行了工艺研究和分析，提出了改进结晶器结构 和工艺参数等措施，实现对含铬铜合金采用水平连铸工艺制管生产。 关键词：铜合金；毛坯管；水平连铸；工艺改进 中图分类号：TG249．7 文献标识码：B 文章编号：1673—3320(2009)06—0017一O2 Discussion on Continuous Cast Process for Rough Tube of Cr-Cu Alloy Drawing Sun Guochen (RD Center,FAW Foundry Co．，Ltd．，Changchun 1 30062，Jilin，China) Abstract：The characters for rou【gh tube castings of Cu alloy by centrifugal cast technology,horizontal continuous cast technology and squeezing cast technology were introduced．The technical questions in the process of horizontal continuous cast for drawing tube were analyzed and studied，the methods how to ireprove the structure of mold and process technical parameters were proposed。the process of CU—Cr alloy tube drawing by hofizontal continuous cast technology was realized． Key words：CU alloy；rough tube casting；horizonml continuous cast：technical improvement 铜基合金因其良好的摩擦系数和力学性能， 形中空零件时，可以省去型芯。但离心铸造铸 作为同步器齿环材料获得广泛应用。齿环毛坯通 出的筒型铸件内孔尺寸不够准确，有较多气 常采用离心铸造、水平连铸、压力挤制等方法获 孔、夹渣，因此需增加内孑L加工余量，而且不 得，其中以水平连铸方式铸造管坯应用最广。近 适宜浇注容易产生密度偏析的合金。离心铸造 年来，由于对同步器齿环性能要求的提高，实际 投资少、见效快，适合科研试验和规模较小企 生产中在铜合金中加入高熔点、高耐磨元素，如 业【¨。 Cr、Ni、Co、Ti等，以获取更好的力学性能。在 1．1．2 水平连铸 毛坯生产过程中，发现铜合金中加入Cr元素后， 水平连铸工艺因其是在液面下过水铸造， 合金液黏稠度变大，以常规工艺参数水平连铸拉 产品品质好，并具有冷却迅速、晶粒细化的特 拔含铬铜合金管坯非常困难，裂纹、气孔等缺陷 点。该工艺易于实现机械化、自动化，生产效 严重，难于投入批量生产。本文对产生这一问 率高，劳动强度低；工艺出品率高，原材料消 耗低；适合大批量、自动化生产，为大多数厂 题的原因进行具体分析和探讨，提出工艺改进措