可锻铸铁电瓷铁帽铸件的质量控制.pdfVIP

学兔兔 Ju1．2009 铸 造 V0I．58 NO．7 F0UNDRY 可锻铸铁电瓷铁帽铸件的质量控制 马永杰，汪 洋 (商丘职业技术学院机电工程系，河南商丘476000) 摘要：为达到可锻铸铁电瓷铁帽的力学性能指标要求，在生产中通过采用控制其化学成分、炉料、修炉、加料、熔炼 操作、热处理、力学性能检测等一系列的措施。在采取上述措施后，铸件的力学性能稳定，且满足使用要求。 关键词：可锻铸铁；电瓷铁帽；质量控制 中图分类号：TG254 文献标识码：B 文章编号：1001—4977(2009)07—0737=03 Quality Control of Malleable Cast Iron Electric Porcelain Cap MA Yong-jie，WANG Yang (Department of Electrical and Mechanical Engineering，Shangqiu Polytechnic College， Shangqiu 476000，Henan，China) Abstract：To meet the mechanical properties requirements of malleable cast iron castings．of the electric porcelain cap，many measures were adopted in production，such as controls of the chemical composition，charge，furnace repairing，feeding and melting operation，as welI as heat treatment and test of the mechanicaI properties。By using of the above measures．the mechanicaI properties of the castings are stable and meet the operating requirements． Key words：malleable cast iron；electric porcelain cap：quality control 高压线路悬式绝缘子一 电瓷铁帽在工作时主要承 型钢的废钢，防止含有铬、钛、砷等合金元素的废钢 受拉应力，广泛应用铁素体基体可锻铸铁KTH350—10来 混入，以免影响退火质量，造成力学性能不合格。炉 铸造，因其具有高的强度和良好的减震性、塑性和韧性。 料的块重、块度的影响。块重越大，热量由表面传到 壁厚为3～l0mm，单重为1~3 的电瓷铁帽，我们使用 中心的时间越长，越易造成棚料。因此块重控制在 3．5 t／IE排风口热风炉胆冲天炉熔炼铁液、湿粘土砂脱箱 1～1．5 kg，块度控制在不大于炉径的1／3为宜。 手工造型、燃煤台车式热处理炉退火，炉前化学分析法 2．2 焦炭 进行化验。要满足电瓷铁帽材质长期稳定达到牌号所要 由于可锻铸铁的碳、硅含量低，铸态是白口组织， 求的力学性能指标，即：R ≥350 MPa，A≥10％， 铸造焦炭的固定碳含量、强度指标高，块度80～1 20 mm， HB160，对材质的控制要从以下几个方面进行分析。 在焦铁比1：(6~7)、冲天炉风、焦平衡操作情况下，可使 出铁温度稳定达到1 420～1 450℃。