原砂粒度分布与碱性酚醛树脂砂抗压强度的关系.pdfVIP

学兔兔 原砂粒度分布与碱性酚醛树脂砂抗压强度的关系 叶永姣 (中核苏阀横店机械有限公司，浙江 横店 3221 18) 摘要：在相同型砂配比和试验条件下，分析了原砂粒度分布与碱性酚醛树脂砂抗压强度的关 系。试验结果表明，3O～5 0目和4 0～70目的原砂最适合于碱性酚醛树脂砂工艺，可减少碱性酚 醛树脂的用量，降低生产成本，提高铸件质量。 关键词：碱性酚醛树脂；抗压强度；原砂；粒度分布 中图分类号：TG221,4-．2 文献标识码：A 文章编号：1673-3320(2014)05-0007—02 Relationship Between Grain Size Distribution of Base Sand and Compressive Strength of Alkaline Phenolic Resin Sand YEYongjiao (Heval Hengdian Machinery Co．，Ltd．CNNC，Hengdian 322118，Zhejiang，China) Abstract：The relationship between grain size distribution of base sand and compressive strength of alkaline phenolic resin sand was analyzed at the same sand formula and test conditions．The test results show that the base sand wim 30．50 mesh or 40．70 mesh is most suitable for alkaline phenolic resin sand process，which can decrease the amount of alkaline phenolic resin，reduce production cost，and improve the quality of castings． Key words：alkaline phenolic resin；compressive strength；base sand；grain size distribution 收稿日期：2014—02—28 作者简介：叶永姣 (1973一)，女，注册质量工程师，主要从事铸钢生产和理化分析的质量管理工作 生产的无机湿态覆膜砂，原先使用的醇基涂料喷 砂型 (芯)的侵蚀最小。涂料自然风干，快干效 涂后砂芯存放一天即大量变形，经分析为普通醇 果明显。 基涂料含水量过高所致。改用CITEK专用快干涂 料，喷涂涂料后的砂芯可保存七天以上，且砂芯 参考资料： 变形量都在允许范围内。 【1】中国机械工程学会铸造分会．铸造手册：第4卷造型材料 [M]．北京：机械工业出版社，2002． CITEK专用快干涂料经大批量使用，浇注后 [2】柳百成，黄天佑．中国材料工程大典：第18／19卷材料铸造 表面的涂层能成片剥离，铸件表面光洁。 成形工程[M]．北京：化学工业出版社，2006． [3】陈国桢，肖柯则，姜不居．铸件缺陷和对策手册[M】．北京： 5 结论 机械工业出版社，1996． 1)耐火粉料的粒度级配是涂料形成烧结剥离