以硅溶胶为粘结剂的硅基陶瓷型制备工艺研究.pdfVIP

维普资讯 学兔兔 May2008 VOI．57 NO．5 以硅溶胶为粘结剂的硅基陶瓷型制备工艺研究 袁新强 (陕西理工学院材料科学与工程学院，陕西汉中723003) 摘要：主要研究了以硅溶胶为粘结剂的硅基陶瓷型制备工艺。研究发现，采用NH C1水溶液为催化剂和真空干燥工艺 制备硅基陶瓷型，不仅可避免传统陶瓷型用硅酸乙酯的复杂水解工艺，而且可获得表面质量较好的陶瓷型，成本降低。 同时，硅溶胶浆料的胶凝硬化在1 h内完成。研究表明，硅溶胶可作为陶瓷型制备用粘结剂。 关键词：硅溶胶；硅酸乙酯；硅基陶瓷型；胶凝硬化 中图分类号：TG221 文献标识码：A 文章编号：lOOl一4977(2008)05—0458—03 Preparation Process of Silica Based Ceramic Mold Using Silica Sol as Binder YUAN Xin—qiang (School of Materials Science and Engineering，Shaanxi University of Technology， Hanzhong 723003，Shaanxi，China) Abstract：The present investigation iS foCUS on the preparation process of silica．based ceramic mold using silica s0l as binder．Results show that taking NH4Cl solution as catalyst and using vacuum drying process to fabricate silica based ceramic mold not only avoid the complex hydrolyse process of ethyl silicate used in conventional ceramic mold．but also gain the ceramic mold with relative good surface quantity and reduce the cost．Meantime，gel hardening of silica sol slurry may complete in 1 h．Fr0m these results it iS concluded that silica SOl can be used to prepare ceramic mold as binder． Key words：silica sol；ethyl silicate；silica．based ceramic mold：gel hardening 目前，陶瓷型铸造已成为大型厚壁精密铸件生产 不能回溶，成本高。因此，寻求一种可代替硅酸乙酯 的一种重要精密铸造方法。由于陶瓷型铸造生产的模 水解液粘结剂具有重要的市场意义。本研究中，用硅 具具有尺寸精度高、表面粗糙度低、热裂少、模具加 溶胶代替硅酸乙酯水解液成型陶瓷型进行了深入研究， 工周期短、成本低、寿命长等优点，所以被广泛应用 并定义这种陶瓷型为硅基