A201平板铸件健全性与抗拉强度及X光检验关系之探讨.pdfVIP

学兔兔 Jan．2O11 铸 造 VOI．60 NO．1 FO RY A201平板铸件健全性与抗拉强度及 X光检验关系之探讨 郭永圣 (建国科技大学机械工程系，台湾彰化) 摘要：系统改 A201~合金平板铸件的长度、厚度及冒口尺寸，以探讨不同铸造条件下，A20l平板铸件相对位置的 力学性能与x射线检测结果之间的关系，可为冒口设计及金属凝固提供参考。型砂为100％@砂。试验结果表明，A201 铝合金平板铸件的力学强度与X射线照相试片等级不存在绝对的对应关系。 关键词：A201铝合金；抗拉强度；无损检测；X射线检测 中图分类号：TG146．2 1 文献标识码：A 文章编号：1001—4977(201 1)01—0073—04 Soundness Determination of A201 AIUmjnUm Alloy Plate Castings Based on Tensile Strength and X．Ray Test KUO Yeong-sant (Department of Mechanical Engineering，Chienkuo Technology University，Changhua，Taiwan，China) Abstract：The riser size and the casting geometry were systematically changed in this study to find out the relationship between mechanical properties and X—ray test results of the A201 aIuminum alloy plate castings．The sand molds with end chill were made of 1 00％ silica sand．The result shows that the tensile strength does not totally match X—ray grade at the same position of the castings． Key words：A201 aluminum alloy；tensile strength；non—destructive testing；X—ray testing A201铝合金在铸造铝合金中，具有较佳的抗拉强 度为386 MPa；亦有研究以抗拉强度判定铸件的健全性 度及屈服强度，目前已广泛应用于航天及兵器领域中， 时，设定当铝铜系列铸件抗拉强度超过372 MPaH~，则 但因其具有124～127℃的宽凝固范围_11，使其铸造性能 判定铸件为健全[71。 不~1A356、A357等铝硅系列合金优良，极易产生铸造 对于微孔隙量与抗拉强度之间的关系，微孑L隙量越 缺陷，例如缩裂、微孔隙、冷接等；以往研究曾对 高，抗拉强度越差，这已获得证实 。但是，对于抗拉 A201铸件的力学性能进行广泛的探讨 。 强度与x射线照相试片之问的关系，则未见讨论。本研 对铸造工作者而言，铸件能否使用，除要进行传 究对A201铝合金平板铸件试片的抗拉强度与x射线照相 统的破坏性检验，例如力学性能试验、疲劳试验、金 试片等级之间的关系进行探讨。A20I铝合金中，Ag含 相观察等外，对铸件本身亦常进行无损检测 (NDT)。 量为0．4％～1．0％，这是A201铝合金价格昂贵的主因，银 运用最为广泛的是x射线检验，尤其对于航天及军事 含量越高，其价格越贵。比较A206铝合金，