柔韧性环氧树脂堵漏材料的研究.pdfVIP

学兔兔 全国中文核心期刊 新癯 巍 中国科技核心期刊 柔韧性环氧树脂堵漏材料的研究 杨晓强，王彦臻，陈千 (西安市地下铁道有限责任公司，陕西 西安 710018) 摘要：采用低分子多胺、多聚甲醛与长链酚的曼尼斯反应合成酚醛胺，再配以聚醚胺和促进剂制备柔韧性环氧树脂固化剂，同 时通过共混改性的方法对环氧树脂进行改性，制备一种柔韧性环氧树脂堵漏材料。研究了活性稀释剂、增韧剂和固化剂含量对环氧 堵漏材料性能的影响。通过配方的优化，得到了可灌性好、性能优异的堵漏材料。 关键词：环氧树脂；柔韧性；堵漏材料 中图分类号：TU57 文献标识码：A 文章编号：1001—702X(2016)01—0056—03 Study on the flexible epoxy resin sealing material YANG Xiaoqiang，WANG Yanzhen，CHEN Qian (Xian Mass Transit Railway Co．Ltd．，Xi an 710018，China) Abstract：A kind of flexible epoxy resin curing agent was prepared by mixing phenolic amine，poly formaldehyde and promot— er．The phenolic amines ware synthesized by Mannich reaction of low molecular polyamine，polyamine and long chain pheno1．At the same time，the epoxy resin was modified by blending modification method．Then，a kind of flexible epoxy resin sealing material was prepared．The effect of the content of reactive diluent，toughening agent and curing agent on the properties of epoxy resin sealing material was studied．Through the optimization of the formulation，a new sealing material with good irrigation and excellent perform ance was obtmned． Key words：epoxy resin，flexible，sealing material 环氧树脂堵漏材料一般分为A、B组分，A组分以环氧树 O 前 言 脂为主体，B组分为固化剂，通常使用的固化剂为小分子多元 随着国民经济的快速发展，我国城市地铁建设十分迅速。 胺，其反应速度快、可室温固化，但是分子量较低、挥发性大、 地铁工程设计的使用寿命长达百年，然而受地质条件的不同， 毒性大，对人体伤害也大。由于反应速度过快，使固化收缩应 新旧结构的搭接，地铁隧道不同施工工艺的结构之间的结合， 力大、易开裂、性脆。并且固化剂用量少，配比要求严格，给使 混凝土自身的收缩，施工质量，地下水等因素的影响，造成地 用者带来不便啕。本文采用低分子多胺、多聚甲醛与长链酚的 铁混凝土结构的裂缝、变形缝、施工缝及缺陷等不可避免地存 曼尼斯反应，制备柔韧性的酚醛胺固化剂，克服了传统小分子 在一定程度的渗漏水，给地铁的安全运