学兔兔 全国中文核心期刊 新 巍 外加剂复合聚合物防水砂浆的制备 高淑娟 (常州工程职业技术学院，江苏 常州 213164) 摘要：通过将羟丙基甲基纤维素醚、高效减水剂、消泡剂、引气剂、防水剂及膨胀剂等外加剂复掺进行试验，探索不同外加剂在 砂浆中的合理掺量，使制备的砂浆具有较好的保水增稠性能，满足现场施工要求；28 d抗压强度在24 MPa以上，28 d抗渗压力大于 1．6MPa，符合JC／T984--2005《聚合物水泥防水砂浆》标准规定。 关键词：聚合物防水砂浆；外加剂：抗渗压力 中图分类号：TU578．12 文献标识码：A 文章编号：1001—702X(2010)08—0070—03 Preparation of the polymer waterproof mortar by compounding additives GA0 Sh Mm (Changzhou Institute of Engineering and Technology，Changzhou 213164，Jiangsu，China) Abstract：Pilot studies of MECELLOSE，high efficient water reducer，foam suppressor，air entraining agent，waterproof agent，ex— panding agent and other additives on the properties of polymer waterproof mortar were conducted to investigate the best dosage of various additives，SO as to make the prepared mortar have better water—thickening properties，capable of meeting the on-site con— stmction requirements 28 d compressive strength is above 24 MPa,28 d impermeability pressure is higher than 1．6 MPa，whic h is in accordance with the standard JC／T 984--2005“Polymer Cement Waterproof Mortar． Key words．polymer waterproof mortar；additive：impermeability 表1 试验用42．5级普通硅酸盐水泥的基本性能 O 前 言 细度 密度，比表面积抗折强度，MPa抗压强度 P丑凝结时间 n 近几年，城市地下空间的大规模开发应用，以及大量地下 ／％ (g／cm~)／(m2／kg) 28d 28d 人防工程的修缮和恢复利用，其防水工程多采用刚柔结合、多 2．U j．U 440 6．2 l2．7 2U．4 47． l 275 道设防的背水面施工，因此，防水性砂浆类产品具有很大的市 1．2 黄砂 场需求。但是通过在工程中的应用发现，刚性防水砂浆产品存 黄砂的细度模数为2．