聚羧酸高效减水剂对胶砂蒸养强度的影响.pdfVIP

学兔兔 2011年第9期 混 凝 土 与水 泥制 品 201 1 N09 9月 CHINA C0NCRETE AND CEMENT PR0DUCTS September 聚羧酸高效减水剂对胶砂蒸养强度的影响 何志旗，伍勇华，南 峰，何廷树 (西安建筑科技大学材料科学与工程学院710055) 摘 要：研究了聚羧酸高效减水剂单掺及与早强剂和消泡剂复掺对胶砂试件蒸养强度的影响。试验结果表明： 水灰比相同时，单掺聚羧酸高效减水剂由于缓凝和引气作用，会显著降低胶砂试件的蒸养强度，而掺入早强剂和消 泡剂可明显改善这种不利影响。降低水灰比并严格控制水灰比，是聚羧酸高效减水剂应用于蒸养混凝土的关键。 关键词：聚羧酸高效减水剂；早期强度；蒸汽养护；缓凝；引气 Abstract：The effects of adding poly—carboxylic acid superplasticizer alone and adding together with early strength a— gent and defoaming agent oil the steam-cured strength of mortar specimens are studied．The results show that with the same water—cement ratio，because of the retarding and air entraining effects of poly-carboxylic acid superplasticizer，the steam-cured strength of mortar specimens will be obviously reduced when adding poly—carboxylic acid superplasticizer alone，but the compound mixture of poly-carboxylic acid superplasticizer with early strength agent and defoaming agent can apparently improve the negative impact．Reducing the water—cement ratio，and controlling the water—cement ratio strictly are the keys to the application of poly—carboxylic acid superplastieizer on steam—cured concrete． Key words：Poly—carboxylic acid superplasticizer；Early strength；Steam curing；Retarding；Air entraining 中图分类号：TU525．9 文献标识码：A 文章编号：100O一4637(2O1 1)09-13-04 0 前言 1 试验 聚羧酸高效减水剂作为新型高效减水剂在土 1．1 原材料 建工程的现浇 昆凝土中已有广泛应用。聚羧酸高效 试验所用水泥为陕西某厂生产的42．5级早强 减水剂减水率高，可降低胶凝材料用量；使用聚羧 型普通硅酸盐水泥，其性能见表1。 酸高效减水剂的混凝土可添加更多的矿渣或粉煤 试验所用河砂为西安灞河中砂，细度模数为 灰取代水泥，从而降低成本，还可提高混凝土的弹 2．66，含泥量为2％。 性模量并降低混凝土收缩开裂的倾向『l】，因此，聚羧 聚羧酸高效减