磨细钢渣粉对水泥混凝土性能影响的研究.pdfVIP

学兔兔 2012年第5期 混凝土与水泥制 品 2012 No．5 5月 CHINA C0NCRETE AND CEMENT PR0DUCTS Mav 磨细钢渣粉对水泥混凝土性能影响的研究 蔡琪瑛 (中交一公局厦门工程有限公司，361021) 摘 要：研究了磨细钢渣粉的掺量对水泥胶砂和水泥混凝土工作性与强度的影响，以及钢渣粉和粉煤灰不同比 例复掺对混凝土性能的影响。结果表明，磨细钢渣粉在一定程度上可以改善混凝土的工作性，降低混凝土的强度，钢 渣粉掺量不宜大于30％；钢渣粉与粉煤灰复掺可以发挥超复合效应，配制出C40以上的高性能混凝土。 关键词：钢渣粉；混凝土性能；掺量；复掺 Abstract：The effects of the dosage of ground steel slag on workability and strength of cement colloidal mortar and concrete are studied，and the effects of combined mixture of steel slag and fly ash on the performances of concrete are re— searched．The results show that the ground steel slag can improve the workability of concrete to some extent and decrease its strength，and the dosage of steel slag should be no more than 30％．Combined mixture of steel slag and fly ash can play composite effects to prepare high perform ance concrete with the strength grade more than C40． Key words：Steel slag；Performances of concrete；Dosage；Combined mixture 中图分类号：TU528．041 文献标识码：A 文章编号：1000—4637(2012)05一O5—04 0 前言 1 试验原材料 钢渣是炼钢过程中产生的一种工业废渣，一般 1．1 水泥 为粗钢产量的15％～20％。2010年，全国粗钢产量6 P·0 42．5级水泥，其力学性能见表1。 亿多吨，按该比例推算，每年将产生近亿吨的钢渣。 表 1 水泥的主要力学性能指标 大量钢渣的堆积不仅占用土地，而且容易造成环境 抗压强度／MPa 抗折强度／MPa 的污染。钢渣中含有一定数量的C，S、C S等，其矿物 组成与水泥的化学矿物组成比较相似，具有潜在的 水化活性，属于具有较大开发利用潜力的资源 _3_。 与矿渣和粉煤灰相比，矿渣的利用率近乎100％，Ⅱ 1．2 钢渣粉 级粉煤灰的利用也比较普遍，而钢渣由于其化学成 所用磨细钢渣粉为转炉钢渣，其化学组成见表 分、矿物组成波动大，粉磨困难，长期安定性差，活 2，主要物理和力学性能见表