适于热带连续退火的OCr17Al的工艺和性能研究.pdfVIP

2009’高品质特殊钢技术与市场论坛 7A 适于热带连续退火的OCrlI的工艺和性能研究 郎宇平，荣凡，陈海涛 (钢铁研究总院结构材料研究所北京100081) 摘要：本文研究了OCrl7A1连铸坯组织，退火工艺对热轧带组织性能的影响。结果表明：成分均匀，等轴晶比例在55％的连 在980。C以上。含Al钢的热带连续退火最适宜的温度为950一1000℃。 关键词：OCrl7A1，连续退火，A1N夹杂 Researchonthe and of0Crl7Alforcontinuous processesproperties annealing Haitao Lang Fan，Chen Yuping，Rong Ironand (Central SteelResearch 100081) Institute，Beijing ofcontinuous Abstract：themicrostructures slabofOCrl7Alandtheinfluenceof forthemicrostmcrures casting annealingprocess and havebeen shownthat witll ofhot researched．11”results continuousslab about55％ propertiesrollingstrip homogenouscasting is for mechanicaland O．15％aluminiom about the ofAI equiaxedgrainnecessarygood propertiesformability．With temperature Increasesto1000℃andthe ofa+1，isreduced．Whenthe afterhot isabove900℃the up phaseregion annealingtemperaturerolling AIN full ofhot the shouldbeabove980℃．The recrystallizationhappened．Forreducing rollingstrip temperature optimum annealing continuous forhot of0Crl7AIis950℃tol000℃． annealingtemperaturerollingstrip Keywords：0Crl7Al，continuousannealing，AIN 1、前言 标准430(OCrl7)铁素体不锈钢是当前广泛应用的不锈钢牌号，主要应用领域包括厨房设备、家电、 民用五金、建筑装簧以及汽车工业等各个行业，其使用量在不锈钢中仅次于304奥氏体不锈钢【l】。但传统 的430不锈钢的生产工艺和冷成形性能尚存在下列弊病：(1)由于钢的成分特殊，决定了它的热带必须采 用罩式退火炉进行退火，通常在800℃～850℃保温8