高压绕管式换热器中换热管漏气后的返修..docVIP

高压绕管式换热器中换热管漏气后的 返修 张 庆 生 （开封东京空分集团有限公司，河南省开封市北关街8号 475001） 摘 要：从某套空分设备上卸下的DR87XX型高压绕管式换热器的换热管胀接部分焊缝出现漏气现象，原因是胀接压力过大，制定了详尽的返修方案，具体实施后高压绕管式换热器恢复正常运行。文章简介了DR87XX型高压绕管换热器中换热管与管板的 “贴胀+强度焊”的模 Repair of the leakage of heat exchanger pipe in high pressure spiral tube heat exchanger Zhang Qing-sheng (Kaifeng Dongjing Air Separation Group Co., Ltd., 8 Beiguan Street, Kaifeng 475001, Henan, P. R. China) Abstract: From a certain empty cent equipments up unload of the DR87 XX type high pressure rounded tube type to change a hot machine to change hot tube the bulge connected parts of welds sew appear to leak air phenomenon, reason is the bulge connected pressure over big, draw up in details returned to fix a project, concrete implement empress the high pressure round tube type change the hot machine instauration normally circulate.The article brief introduction the DR87 XX type the high pressure rounds the mode that the tube changes to change a hot tube and tube the knotholestick bulge+ the strength weld in the hot machine, detailed describe to return bulge of fix the front to connect to experiment,examination with return to fix the craft process, tallied up to return to fix finally medium of regulation.. Key words: High-pressure spiral tube heat exchanger；Heat exchange pipe；Repair；Expansion；Strength weld；Expanding test —————— 从某套空分设备上卸下的DR87XX型高压绕管式换热器，检测后发现换热管胀接部分焊缝出现漏气，原因是胀接压力过大，使换热管贴胀后内应力大的焊缝，在工作过程中经历裂纹萌生、稳定扩展和失稳扩展三个阶段，出现疲劳裂纹，疲劳裂纹宏观断口呈脆性，无明显塑性变形，在断口上可观察到裂纹源，光滑或贝壳状的疲劳裂纹扩展区和粗糙的瞬断区，造成隔层之间相互漏气，既影响产量，又影响纯度。换热器先胀后焊“贴胀+强度焊”的模 通过贴胀，能有效地阻尼振动对焊口的损伤，避免间隙腐蚀间隙腐蚀?在前应，通过试胀，检验头的密封性能，测试胀接接头的拉脱，选定最佳胀接，待时采用。 （2）换热管胀接前，对试验件的换热管进行编号（硬印或记号笔）以示区别，并测量每根换热管端部外径、内径及相对应的管板孔内径，（见表1）。 表1 不锈钢钢管-钢制管板胀接试验记录： 接头号 尺 寸 1 2 3 4 5 胀前管外径 mm 24.95 24.9 24.9 24.9 25.0 胀前管内径 mm 20.9 20.9 20.9 20.9 21.0 管壁厚mm 2.05 2.0 2.0 2.0 2.0 胀后管内径mm 21.3 21.5 21.6 21.8 21.9 胀接压力MPa 79 100 120 141 160 拉脱强度MPa 0.8 1.1 1.3 1.5 1.7 注：1）在