超磁致伸缩材料的冶炼铸造工艺研究.pdfVIP

第 5 卷 第 6 期 金属功能材料 Vol . 5 No . 6 1998 年 12 月 Metallic Functional Materials December 1998 超磁致伸缩材料的冶炼铸造工艺研究 杜 　挺 　张洪平 (钢铁研究总院工艺所 　北京 　100081) 摘 　要 　用作者研制的电弧冶炼铸造设备进行了超磁致伸缩材料的冶炼铸造工艺研究 。经过大 量熔铸试验说明该设备较简单 , 冶炼铸造工艺合理 , 时间短 ,成本低 , 能制备 6 ～ 15 ,长 10 ～ 110mm 的多晶合金棒 。合金回收率可达 8957 %～9662 % ,稀土元素烧损率可控制在 4 55 %～ 12 33 %范围内。 关键词 　超磁致伸缩材料 　冶炼铸造工艺 　合金回收率 　稀土烧损率 Melting and Casting Technologies of Giant Magnetostrictive Material s D u Ti ng 　　　Zhang Hongp i ng ( jing 100081) Central Iron Steel Research Institute , Bei ABSTRACT 　The melting and casting technologies for producing giant magnetostrictive materials have been studied using t he arc melting - casting furnace develop ed by t he aut hors. The polycrystal alloy rods wit h t he size of 6～15mm in diameter and 10～100mm in lengt h are produced . A number of exp eriment inducate t hat t he equip ment is simple , t he technologies are suitable , time is short and t he cost is low . The alloy yield can be reached to 8957 %～9662 % and t he rare eart h lost can be controlled wit hin t he range of 4 55 %～12 33 % 。 KEY 　WORDS 　giant magnetostrictive material , melting - casting technlologies , alloy yield , rare eart h lost 　　稀土铁系超磁致伸缩材料的冶炼工艺研 磁致伸缩系数已提高到 目前的 2400 ×10 - 6 , 究一直受到人们的普遍关注 , 特别是超磁致 即使有相同的配料成分 , 由于其冶炼工艺的 伸缩材料棒的制备工艺 。在棒的制备工艺方 改变 , 或制备工艺的改变 , 都将影响合金的 面 , 国外已有数篇专利发表 , 可见人们对超 显微组织结构和夹杂情况 , 从而影响其磁学 磁致伸缩材料冶炼工艺的重视 ,