双组分道路标线涂料的制备与应用.pdfVIP

New Products and New Technology 新产品 新工艺 双组分道路标线涂料的制备与应用 □ 窦小燕,潘 峰 (新疆公路规划勘察设计研究院,乌鲁木齐 830006) 摘要：采用活性丙烯酸树脂与丙烯酸单体为基体,用引发剂交联固化,制备出具有黏度低、固体 含量高、固化时间适宜、低污染、耐磨、与玻璃珠粘结牢固、耐候性好等特点的双组分道路标线涂 料。着重讨论涂料配方中的树脂、活性单体、钛白粉的用量及填料粒径的合理级配。 关键词：标线涂料；双组分；配方 + 中图分类号：TQ630.7 9 文献标识码：A 文章编号：1006-2556(2009)02-0040-04 Preparation and use of two-package road mark coatings Dou Xiaoyan, Pan Feng (Xinjiang Institute of Highway Panning, Investigation and Design, Urumchi 830006, Xinjiang Uygur Autonomous Region) Abstract: Active acrylic resin and acrylic monomer are used as base materialcrosslinked by initiator to give two-package road mark coatings with low viscosity, high solid content, suitable curing time, low pollution, wear resistance, i rm bonding with glass bead and good weatherability; and the use amount of resin, active monomer and titanium dioxide and the reasonable gradation of i ller particle size are discussed emphatically. Keywords: road mark coatings, two-package, compositions 0 前 言 随着我国公路建设的迅猛发展和公路交通的日 料,但因其含有有机溶剂,耐候性差且施工不便,故 趋繁忙,交通标线的划设量猛增。目前大量使用的 没有得到推广应用。本试验则选用耐候性好、污染 是热熔型标线涂料,虽然使用寿命较长,但施工时需 少的活性丙烯酸树脂与丙烯酸单体,在引发剂的作 要将涂料加热到200 ℃左右,不仅耗用燃料,且存在 用下交联成涂层。 安全隐患。而对积雪较重的北方城市而言,2 mm厚 1.2 涂料参考配方(见表1) 的热熔标线涂层易被扫雪机铲坏,对磨损的标线重 1.3 树脂合适用量试验 新划设时,残留的涂层又很难清除,费工又费时,因 表1 涂料参考配方 此需要研制能够节能减排、耐用且反光效果好的, A组分 W/% B组分 W/% 适合积雪地区使用的标线涂料。 树脂A 35～50 树脂B 3