棒材连轧生产线低温轧制的可行性分析.pdfVIP

Vol26 No2 12 ENERGY FORMETALLURGICAL INDUSTRY M ar2007 * 郑治龙 王 华 王晓东 (昆明理工大学材料与 金工程学院) 棒材连轧生产线可采用低温轧制工艺实现节能降耗。通过热模拟试验回归出了变形 阻力模型, 建立了轧制过程温度模型并计算出了轧机负荷。金相试验表明, 适当降低轧制温 度有利于晶粒的细化, 从而改善钢材的力学性能。 低温轧制 变形阻力 轧机负荷 Analysis of feasibility for low tem perature rolling on continuous rod m ill Zheng Zhilong WangHua WangXiaodong (Kun ingUniversity ofScience and Technology) A bstract Low te perature rolling technologywas applied for continuous rod production line in order to reduce energy consu ing. The odelofdefor ation resistancewas deduced according to heat si u lation experi ent, the te perature odel was established and ill load was calculated on rolling process in this paper. M etallographic experi ent indicate that reducing the rolling te peratureproper ly is propitious to thin crystal, consequently the echanical perfor ance of steel products is also i proved. K eyw ord s low te perature defor ation resistance ill load 可行性, 以期达到节能降耗和改善产品性能的目 1 的。 棒线材连轧机上,从开轧至终轧,轧件温降很 2 小,甚至升温。在生产实践中经常出现因终轧温 度过高而导致产品质量下降或螺纹钢成品孔型不 由于低温轧制要求轧机负荷必须满足要求, 能顺利咬入等问题。故棒线材连轧机具有实现低 因此如何确定轧件在低温轧制条件下的变形阻力 温轧制的条件。低温轧制不仅可以降低能耗, 还 显得非常重要。为了推导出准确的变形阻力模 〔1〕 可以提高产品质量,创造很大的经济效益 。 型, 作者在攀钢研究院检测中心的 Gleeble- 在轧机负荷允许的情况下, 适当降低轧制温 3500热模拟试验机上完成了模拟试验。测定了 度会使轧件的晶粒组织细化, 力学性能得到改 试样的变形阻力和应力-应变曲线, 回归出了变 善。本文通过热模拟试验测定了低合金钢的变形 形阻力模型。 阻力并对其组织性