载BMP-2基因PLGA微球的制备、表征及在体内异位成骨的实验研究.docVIP

 载 BMP-2 基因 PLGA 微球的制备、表征及 在体内异位成骨的实验研究# 乔春燕1，张恺2，金晗1，苗雷英1，袁安亮1，史册1，孙宏晨1** 5 10 15 （1. 吉林大学口腔医学院，长春 130021； 2. 吉林大学超分子结构与材料国家重点实验室，长春 130021） 摘要：针对多种原因引起的骨吸收问题，制备携带 BMP 基因的纳米磷酸钙与聚乳酸聚羟基 乙酸共聚物（PLGA）的微粒, 利用复合材料缓慢释放 BMP 基因磷酸钙和细胞吞噬后表达 BMP 蛋白的特性, 制备一种具有促进骨再生的载基因复合材料。运用 W/O/W 复乳溶剂蒸发 法制备了载 BMP 基因的 PLGA 微球，分析了 PLGA 分子量、微球粒径等条件对载基因 PLGA 微球释放性能的影响，采用软 X 线和组织学技术观察所制备的载 BMP 基因 PLGA 复合微球 植入 Wistar 大鼠肌囊内的骨形成情况。SEM 结果显示载 BMP 基因微球尺寸为 0.5～35 μm。 包封率可达 30～50%。24 h 内突释率＜7.5%，30 天内累积释药量为 46.8%体内实验，8 周时 实验组软 X 线检查可见明显高密度影，组织学观察植药部位可见大量的骨髓样细胞、成骨 样细胞和骨样组织。利用 W/O/W 复乳溶剂蒸发法制备的载 BMP 基因的 PLGA 微球在非骨 组织区域实现了异位成骨。 关键词：骨再生；磷酸钙；BMP 基因；聚乳酸聚羟基乙酸共聚物 中图分类号：R780.2 20 Preparation and Characterization of PLGA Microspheres Loading pBMP-2 and Its Effects on Ectopic Bone Formation in Vivo QIAO Chunyan1, ZHANG Kai2, JIN Han1, MIAO Leiying1, YUAN Anliang1, SHI 25 30 35 40 Ce1, SUN Hongchen1 (1. School of Stomatology, Jilin University, Changchun 130021; 2. State Key Laboratory of Supermolecule Structure and Material, Jilin University, Changchun 130021) Abstract: The aim of this work was to sythensize the poly(lactic-co-glycolide) PLGA microspheres loading BMP plasmid DNA(pBMP) to obtain ectopic bone formation. First, prepare the CaPi-pBMP coprecipitation composite and then encapsulate them into PLGA microspheres use a water-oil-water emulsion solvent evaporation method. We examined the morphology of PLGA microspheres loading pBMP composite by SEM, quantified the entrapment efficiency and brust release through the nanodrop. We septically placed the PLGA microspheres loading pBMP into a thigh muscle pouch, utilize the soft X-ray and histology to evaluate its effect on ectopic bone formation in vivo. PLGA microspheres loading CaPi- pBMP prepared in this study were spherical in shape with size range of 0.5-35μm, and entrapment efficiency 30–50%. The release of CaPi-DNA from microspheres showed a low burst release (7.5%) within 24 h and following sustained release process,cumulative release of 30 days is 46