某2500m3高炉炉缸侧壁温度异常原因分析及其应对措施.pdfVIP

3 某 2500m 高炉炉缸侧壁温度异常原因分析及其应对措施 1 吴 桐 唐建春 （宝钢设备检修有限公司，上海 201900 ） 摘 要 本文对某 2500m3 高炉炉缸冷却壁第二、三段出现温度异常偏高的状况和产生原因进行了论述和分析。通 过对压浆技术进行了相应的阐述和分析，认为采用压浆技术来进行维护，可以达到降低炉缸侧壁温度的效果。从实 施的效果可以看出，所采取的炭胶压入应对措施很好地解决了高炉炉缸侧壁温度异常的问题，实现了高炉的长期平 稳生产。 关键词 高炉 炉缸侧壁 温度异常 压浆技术 Analysis on Causes of the Abnormal Temperature of Hearth Sidewall for a 2500m3 BF and Its Countermeasures Wu Tong Tang Jianchun （Shanghai Baosteel Equipment Maintenance Co.,Ltd.,Shanghai, 201900） Abstract The status that the second and third parts of the hearth of a blast furnace appeared abnormally high temperature and its occurring reasons were discussed and analyzed.The cement pressing-in technology was discussed, and its feasibility for the blast furnace was also analyzed, the results showed that the technology could be available to reduce the temperature of hearth sidewall.In the practice point of view,the relevant measures including the cement pressing-in technology well resolved the problem that abnormal temperature taking place in hearth sidewall of the blast furnace to make the blast furnace operated for long term stable and smooth production. Key words blast furnace, hearth sidewall, temperature anomaly, grouting technique 1 引言 3 国内某高炉第一代炉龄于2004 年 4 月投产，设计有效容积 2500m ，30 个风口 2 个铁口，炉底、炉 缸采用大块炭砖加陶瓷杯型结构，陶瓷杯杯壁外的炉缸大墙采用微孔炭砖(BC-7S) 。炉皮厚度 60mm 的 Q235C 钢板。至 2010 年 6 月已生产 6 年零 2 个月，累计生产生铁量约 1296 万吨，单位炉容生产生铁 3 5184t/m 。 随着冶炼时间的增长，受原料质量波动及产量等因素的影响，高炉炉缸受到一定程度的侵蚀，常发 生炉缸侧壁温度持续升高或居高不下的现象，在很大程度上反映了侧壁内衬厚度的减薄，当炉缸侧壁厚 度减薄到一定程度